Description:
Nitronic 60 / S21800
Nitronic 60 is a nitrogen strengthened austenitic stainless steel, with outstanding strength and resistance to wear and galling. It maintains decent strength up to temperatures of 1800°F and has oxidation resistance similar to that of S.S 309. The general corrosion resistance is between that of S.S 304 and S.S 316.
It is used in the aerospace, food and drug, oil field, petrochemical, surgical and chemical processing industries.
Nitronic 60 Chemical Composition:
Grade | C% | Mn% | S% | P% | Si% | Cr% | Ni% | N% |
---|---|---|---|---|---|---|---|---|
Nitronic 60 | Max 0.10 | 7.0-9.0 | Max 0.03 | Max 0.04 | 3.5-4.5 | 16.0-18.0 | 8.0-9.0 | 0.08-0.18 |
Nitronic 60 Physical Properties:
Grade | Density | Melting Point |
---|---|---|
Nitronic 60 | 8.0 g/cm3 | 1375 °C |
Nitronic 60 Mechanical Properties:
Condition | Tensile Strength | Yield Strength σp0.2/MPa | Elongation | Reduction% | Brinell Hardness |
---|---|---|---|---|---|
Solution Treated | Min 655 Mpa | Min 345 Mpa | Min 35% | Min 55% | Max 241 |
Description:
Nitronic 60 / S21800
Nitronic 60 is a nitrogen strengthened austenitic stainless steel, with outstanding strength and resistance to wear and galling. It maintains decent strength up to temperatures of 1800°F and has oxidation resistance similar to that of S.S 309. The general corrosion resistance is between that of S.S 304 and S.S 316.
It is used in the aerospace, food and drug, oil field, petrochemical, surgical and chemical processing industries.
Nitronic 60 Chemical Composition:
Grade | C% | Mn% | S% | P% | Si% | Cr% | Ni% | N% |
---|---|---|---|---|---|---|---|---|
Nitronic 60 | Max 0.10 | 7.0-9.0 | Max 0.03 | Max 0.04 | 3.5-4.5 | 16.0-18.0 | 8.0-9.0 | 0.08-0.18 |
Nitronic 60 Physical Properties:
Grade | Density | Melting Point |
---|---|---|
Nitronic 60 | 8.0 g/cm3 | 1375 °C |
Nitronic 60 Mechanical Properties:
Condition | Tensile Strength | Yield Strength σp0.2/MPa | Elongation | Reduction% | Brinell Hardness |
---|---|---|---|---|---|
Solution Treated | Min 655 Mpa | Min 345 Mpa | Min 35% | Min 55% | Max 241 |